IA | VIIIA | ||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
1
H
1.008
|
IIA | red:
superconducting at p=0
blue: p-induced
superconductivity at: (--GPa)
Tc=1.17K or 5.4K Tc decreases
or increases with p |
IIIA | IVA | VA | VIA | VIIA |
2
He
4.003
|
|||||||||
3
Li
6.941
17K
(48GPa) |
4
Be
9.012
0.026K |
5
B
10.81
10?
(GPa) |
6
C
12.01
|
7
N
14.01
|
8
O
16.00
0.6K
(98GPa) |
9
F
19.00
|
10
Ne
20.18
|
||||||||||
11
Na
22.99
|
12
Mg
24.31
(GPa) |
IIIB | IVB | VB | VIB | VIIB | VIIIB | IB | IIB |
13
Al
26.98
1.17K |
14
Si
28.09
5K (12GPa) |
15
P
30.97
4.7K (10GPa) |
16
S
32.07
10K (93GPa) |
17
Cl
35.45
|
18
Ar
39.95
|
||
19
K
39.10
|
20
Ca
40.08
(GPa) |
21
Sc
44.96
~0.2K (17GPa) |
22
Ti
47.87
0.4K |
23
V
50.94
5.4K |
24
Cr
52.00
|
25
Mn
54.94
|
26
Fe
55.85
2.2K (22GPa) |
27
Co
58.93
|
28
Ni
58.69
|
29
Cu
63.55
|
30
Zn
65.39
0.88K |
31
Ga
69.72
1.08/6.4K (0/6.4GPa) |
32
Ge
72.61
7K (11.5GPa) |
33
As
74.92
? (GPa) |
34
Se
78.96
6K (13GPa) |
35
Br
79.90
? (?GPa) |
36
Kr
83.80
|
37
Rb
85.47
|
38
Sr
87.62
(GPa) |
39
Y
88.91
~2K (17GPa) |
40
Zr
91.22
0.61K |
41
Nb
92.91
9.26K |
42
Mo
95.94
0.915K |
43
Tc
(98)
7.8K |
44
Ru
101.1
0.49K |
45
Rh
102.9
0.0003K |
46
Pd
106.4
|
47
Ag
107.9
|
48
Cd
112.4
0.517K |
49
In
114.8
3.41K |
50
Sn
118.7
3.72/5.3K (0/16GPa) |
51
Sb
121.8
2.6/3.55K (0/8.5GPa) |
52
Te
127.6
3.3K (5.6GPa) |
53
I
126.9
? (?GPa) |
54
Xe
131.3
|
55
Cs
132.9
~0.2K (12GPa) |
56
Ba
137.3
1.3-5 (5.5-14GPa) |
57
La
138.9
4.8-6K |
72
Hf
178.5
0.218K |
73
Ta
180.9
4.47K |
74
W
183.8
0.013 |
75
Re
186.2
1.7K |
76
Os
190.2
0.66K |
77
Ir
192.2
0.113K |
78
Pt
195.1
|
79
Au
197.0
|
80
Hg
200.6
4.15/3.95K |
81
Tl
204.4
2.38K |
82
Pb
207.2
7.2/3.55K (0/16.6GPa) |
83
Bi
209.8
3.9-7.2K (2.5-2.7GPa |
84
Po
(209)
|
85
At
(210)
|
86
Rn
(222)
|
87
Fr
(223)
|
88
Ra
(226)
|
89
Ac
(227)
|
104
Rf
(261)
|
105
Db
(262)
|
106
Sg
(266)
|
107
Bh
(264)
|
108
Hs
(269)
|
109
Mt
(268)
|
|||||||||
58
Ce
140.1
1.7 5GPa |
59
Pr
140.9
|
60
Nd
144.2
|
61
Pm
(145)
|
62
Sm
150.4
|
63
Eu
152.0
|
64
Gd
157.3
|
65
Tb
158.9
|
66
Dy
162.5
|
67
Ho
164.9
|
68
Er
167.3
|
69
Tm
168.9
|
70
Yb
173.0
|
71
Lu
175.0
0.1K (6GPa) |
||||
90
Th
232.0
1.38K |
91
Pa
(231)
0.43K |
92
U
238.0
0.19K |
93
Np
(237)
|
94
Pu
(244)
|
95
Am
(243)
0.85K |
96
Cm
(247)
|
97
Bk
(247)
|
98
Cf
(251)
|
99
Es
(252)
|
100
Fm
(257)
|
101
Md
(258)
|
102
No
(259)
|
103
Lr
(262)
|